Machining Material Udimet 718

Udimet 718 is a Nickel-based heat resistant superalloy (HRSA) material with a Machinability rating of 10% and Hardness of 42 HRC.

Udimet 718 has 54% nickel and additional alloying elements per the below table.

The main feature of nickel-based alloys is their excellent strength across a wide temperature range combined with good corrosion resistance. In this sub-group, the material standards also define the allowed hardness range, and hardness is a significant factor affecting the machinability (besides the chemical composition).

Udimet 718 is among the hardest of the nickel-based alloys, and accordingly has poor machinability of only 10%

Superalloys should be machined with a positive and sharp cutting edges. Geometries that are suitable for austenitic stainless steel will also work well on HRSA. However, quality manufacturers will have in their catalogs additional geometries that are specifically designed for these challenging materials.

Summery:

  • For general Turning of Material Udimet 718 at stable conditions use a grade with a Very Hard substrate and PVD coating.
  • For general Milling use a grade with a Semi Hard substrate and PVD coating.
  • For detailed carbide grades recommendations, check the Below Chart, or use the Grades Wizrad.
  • Recommended Cutting speed range for turning at stable conditions is 110 - 150 [SFM] / 35 - 45 [m/min].
  • Consider using CBN inserts. Although they cost more than twice, they enable increasing the cutting speed by 2-4 times (relative to carbide). Learn More ⇒
  • Recommended Cutting speed range for milling with stable clamping and short overhang is 80 - 110 [SFM] / 25 - 35 [m/min]
  • For detailed cutting speed recomendations, check the Below Table, or use our Speed and Feed Calculator.

    • Equivalent International Designations for Material Udimet 718

    Standard Name
    sae5383
    wnr2.4668
    dinNiCr19Fe19NbMo
    bsHR8
    anforNC19FeNb

    Chemical Composition for Material Udimet 718

    Element Amount
    Nickel (Ni)54%
    Iron (Fe)19.0%
    Chromium (Cr)18%
    Molybdenum (Mo)3%
    Titanium (Ti)1%
    Aluminum (Al)0.6%
    Carbon (C)0.05%

    Cutting Speeds Recomendations for Material Udimet 718

    * Click on the speeds below for higher precision in specific conditions!

    ApplicationVc (m/min)Vc (SFM)
    Turning35-45110-150
    Milling25-3580-110
    Parting20-3070-100
    Grooving30-40100-130
    Drilling30-40100-130

    Important! The speed estimation is given for an ideal situation:

    • Most suitable carbide grade
    • Stable tool clamping
    • Stable workpiece clamping
    • Good quality raw material
    • A short overhang of the cutting tool.
    • Nominal hardness of the material.
    • etc.
    Click on the speeds in the above table to get better precision for specific parameters
    Or use our Speed and Feed Calculator


    Recommended Carbide Grades for Material Udimet 718

    * If you do nott understand the below table? Read This Explanation to make the most out of it!

    Grade for Turning

    Grade for Parting Off

    Grade for Grooving

    Grade for Milling (Indexable)

    Recommended Insert Cutting Edge Geometry for Material Udimet 718

    Honing Size:0.02-0.05 mm / 0.001-0.002"
    Rake Angle:13° -18°
    Land Angle:Neutral
    Land Width:0.10-0.20 mm / 0.004-0.008"
    Ground Insert:Recommended

    Learn more about carbide inserts Cutting-Edge Geometry Parameters.