- Application Range
- Compatible Grades
- Cutting Speeds
Sumitomo - AC1030U Menu
General Information: | ||
---|---|---|
Brand | Sumitomo | |
Grade Status | Primary | |
Applications | Turning / Parting / Grooving | |
Substrate Class | Semi Hard | |
Coat Type | Thin PVD | |
Post Treat | Y |
From Sumitomo's website:
"New PVD coating ""Absotech® Bronze"" and special substrate are applied. High quality cutting edge realized excellent resistance against adhesion and microchipping and better nished surface."
Application Range for AC1030U
* If you don't understand the below table? Read This Explanation to make the most out of it!
ISO | Material Group | app | pmksort | App | Apps Range | 05 | 10 | 15 | 20 | 25 | 30 | 35 | 40 | 45 |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
P | Steel | T | 0 | Turning | P10 - P30 | P | P | P | P | P | ||||
M | Stainless Steel | T | 1 | Turning | M20 - M40 | M | M | M | M | M | ||||
K | Cast Iron | T | 2 | Turning | K10 - K30 | K | K | K | K | K | ||||
P | Steel | P | 0 | Parting | P10 - P25 | P | P | P | P | |||||
M | Stainless Steel | P | 1 | Parting | M10 - M25 | M | M | M | M | |||||
K | Cast Iron | P | 2 | Parting | K20 - K40 | K | K | K | K | K | ||||
S | Superalloys | P | 4 | Parting | S20 - S40 | S | S | S | S | S | ||||
P | Steel | G | 0 | Grooving | P10 - P25 | P | P | P | P | |||||
M | Stainless Steel | G | 1 | Grooving | M10 - M25 | M | M | M | M | |||||
K | Cast Iron | G | 2 | Grooving | K20 - K40 | K | K | K | K | K | ||||
S | Superalloys | G | 4 | Grooving | S20 - S40 | S | S | S | S | S |
Equivalent Grades for AC1030U
The most compatible grade from each brand!
A higher score (Up to 100%) means the grades are more compatible. A lower score or a particular grade not listed does not mean it is not a good grade. It means that its physical and mechanical properties are less close to AC1030U
Brand | Application | Grade | Substrate | Coating | Gscore |
---|---|---|---|---|---|
Sandvik | Turning | GC1105 | Hard | Thin PVD | 85% |
Iscar | Turning | IC806 | Very Hard | Thin PVD | 80% |
Kennametal | Turning | KCU25 | Semi Hard | Thin PVD | 90% |
Walter | Turning | WKK25S | Semi Hard | PVD | 90% |
Seco | Turning | CP500 | Semi Hard | Thin PVD | 95% |
Tungaloy | Turning | AH725 | Semi Hard | Thin PVD | 95% |
Mitsubishi | Turning | MP9015 | Hard | PVD | 90% |
Sandvik | Parting | GC1105 | Hard | Thin PVD | 85% |
Iscar | Parting | IC808 | Semi Hard | PVD | 95% |
Kennametal | Parting | KCU25 | Semi Hard | Thin PVD | 90% |
Walter | Parting | WSM23S | Semi Tough | Thin PVD | 85% |
Seco | Parting | CP500 | Semi Hard | Thin PVD | 95% |
Tungaloy | Parting | AH725 | Semi Hard | Thin PVD | 95% |
Mitsubishi | Parting | VP20RT | Semi Hard | PVD | 90% |
Sandvik | Grooving | GC1125 | Hard | PVD | 80% |
Iscar | Grooving | IC808 | Semi Hard | PVD | 95% |
Kennametal | Grooving | KC5025 | Semi Hard | PVD | 90% |
Walter | Grooving | WSM23S | Semi Tough | Thin PVD | 85% |
Seco | Grooving | CP500 | Semi Hard | Thin PVD | 95% |
Tungaloy | Grooving | AH725 | Semi Hard | Thin PVD | 95% |
Mitsubishi | Grooving | VP20RT | Semi Hard | PVD | 90% |
Cutting Speed recommendations for AC1030U
How to use our Cutting Speeds Recommendations
- Pay attention that your desired unit (SFM or m/min) is selected!
- Speeds are given for stable conditions of Machine, Tool, and workpiece.
- An empty cell means the grade is not available for the combination of material and application.
- For more specific Cutting Speeds Recommendations use our advanced
SPEEDS AND FEEDS CALCULATOR
Unit Selector:
SFM
m/min
uid | _ | Material Group | Turning (m/min) | Turning (SFM) | Parting (m/min) | Parting (SFM) | Grooving (m/min) | Grooving (SFM) | Milling (m/min) | Milling (SFM) | Driiling (mm/min) | Drilling (SFM) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
s647602deca8c | P | Free-Cut Steel | 170 - 330 | 510 - 1000 | 145 - 285 | 440 - 860 | 135 - 265 | 410 - 800 | - | - | - | - |
s647602deca8c | P | Low Carbon Steel (0.1-0.25%) | 160 - 195 | 480 - 590 | 135 - 170 | 410 - 510 | 125 - 155 | 380 - 470 | - | - | - | - |
s647602deca8c | P | Carbon Steel (0.26-0.50%) | 135 - 195 | 410 - 590 | 115 - 170 | 350 - 510 | 105 - 155 | 320 - 470 | - | - | - | - |
s647602deca8c | P | High Carbon Steel (0.51-1.0%) | 110 - 135 | 330 - 410 | 95 - 115 | 280 - 350 | 90 - 105 | 270 - 320 | - | - | - | - |
s647602deca8c | P | Low Alloyed Steel (180 HB Max) | 170 - 205 | 510 - 620 | 145 - 175 | 440 - 530 | 135 - 165 | 410 - 500 | - | - | - | - |
s647602deca8c | P | Low Alloyed Steel (180-275 HB) | 95 - 170 | 280 - 510 | 85 - 145 | 250 - 440 | 80 - 135 | 240 - 410 | - | - | - | - |
s647602deca8c | P | Low Alloyed Steel (275 -350 HB) | 60 - 95 | 180 - 280 | 55 - 85 | 160 - 250 | 50 - 80 | 150 - 240 | - | - | - | - |
s647602deca8c | P | Tool Steel and High Alloy Steel (Annealed) | 55 - 135 | 160 - 410 | 50 - 115 | 150 - 350 | 45 - 105 | 130 - 320 | - | - | - | - |
s647602deca8c | P | Tool Steel and High Alloy Steel (250-300 HB) | 40 - 95 | 120 - 280 | 35 - 85 | 100 - 250 | 35 - 80 | 100 - 240 | - | - | - | - |
s647602deca8c | M | Ferritic Stainless Steel | 90 - 235 | 270 - 710 | 60 - 155 | 180 - 470 | 80 - 205 | 240 - 620 | - | - | - | - |
s647602deca8c | M | Martensitic Stainless Steel | 90 - 145 | 270 - 440 | 60 - 95 | 180 - 280 | 80 - 125 | 240 - 380 | - | - | - | - |
s647602deca8c | M | Austenitic Stainless Steel | 90 - 120 | 270 - 360 | 60 - 75 | 180 - 220 | 80 - 100 | 240 - 300 | - | - | - | - |
s647602deca8c | M | Duplex Stainless Steel | 25 - 80 | 70 - 240 | 15 - 50 | 40 - 150 | 25 - 70 | 70 - 210 | - | - | - | - |
s647602deca8c | M | Precipitation Hardening St. St. | 105 - 130 | 320 - 390 | 70 - 85 | 210 - 250 | 90 - 115 | 270 - 350 | - | - | - | - |
s647602deca8c | K | Grey Cast Iron (180 HB Max) | 115 - 150 | 350 - 450 | 125 - 170 | 380 - 510 | 90 - 115 | 270 - 350 | - | - | - | - |
s647602deca8c | K | Grey Cast Iron (180-260 HB) | 70 - 120 | 210 - 360 | 75 - 135 | 220 - 410 | 55 - 95 | 160 - 280 | - | - | - | - |
s647602deca8c | K | Nodular cast iron (160 HB Max) | 115 - 165 | 350 - 500 | 125 - 185 | 380 - 560 | 90 - 130 | 270 - 390 | - | - | - | - |
s647602deca8c | K | Nodular cast iron (180-280 HB) | 45 - 110 | 130 - 330 | 55 - 120 | 160 - 360 | 35 - 85 | 100 - 250 | - | - | - | - |
s647602deca8c | K | Malleable cast iron (180 HB Max) | 105 - 160 | 320 - 480 | 120 - 175 | 360 - 530 | 80 - 125 | 240 - 380 | - | - | - | - |
s647602deca8c | K | Malleable cast iron (180-270 HB) | 45 - 105 | 130 - 320 | 55 - 120 | 160 - 360 | 35 - 80 | 100 - 240 | - | - | - | - |
s647602deca8c | S | Iron (Fe) Based - Supper Alloys | - | - | 40 - 85 | 120 - 250 | 60 - 115 | 180 - 350 | - | - | - | - |
s647602deca8c | S | Nickel (Ni) Based - Supper Alloys (20 HRC Max | - | - | 25 - 75 | 70 - 220 | 35 - 105 | 100 - 320 | - | - | - | - |
s647602deca8c | S | Nickel (Ni) Based - Supper Alloys (21-42 HRC) | - | - | 15 - 30 | 40 - 90 | 20 - 45 | 60 - 130 | - | - | - | - |
s647602deca8c | S | Cobalt (Co) Based - Supper Alloys | - | - | 10 - 30 | 30 - 90 | 15 - 45 | 40 - 130 | - | - | - | - |
s647602deca8c | S | Pure Titaium | - | - | 45 - 75 | 130 - 220 | 65 - 105 | 190 - 320 | - | - | - | - |
s647602deca8c | S | Titanium alloys | - | - | 25 - 50 | 70 - 150 | 35 - 70 | 100 - 210 | - | - | - | - |